Amorphous precipitated siliceous pigments and methods for their production

ABSTRACT

A method for producing precipitated silicic acid pigments and silicates having a unique combination of physical and chemical properties is disclosed. The pigments are produced by acidulating a solution of an alkali metal silicate with an acid until precipitation just begins. At this point the reaction mass is aged for a period of time and thereafter the acid addition is continued until the precipitated product is obtained. Pigments produced in accordance with the invention exhibit lower wet cake moisture (or higher percent solids) and are characterized by their low structure, low oil absorption, high abrasiveness and high pack density. The products can be used as abrasive and polishing agents in dentifrice compositions, in the production of molecular sieves, in paints and the like. In a particularly advantageous embodiment, an adduct material, such as aluminum, is added to control the refractive index of the precipitated pigment. Products produced in this manner have particular utility for use as abrasion and gelling agents in clear toothpaste compositions.

United States Patent Wason AMORPHOUS PRECIPITATED SILICEOUS PIGMENTS AND METHODS FOR THEIR PRODUCTION Satish K. Wason, Havre de Grace, Md.

[73] Assignee: J. M. Huber Corporation, Locust,

[22] Filed: Sept. 6, 1972 [2|] Appl. No; 286,655

[75] Inventor:

Primary Examiner-Delbert E. Gantz Assistant Examiner-J. V. Howard Attorney, Agent, or Firm-Harold H. Flanders; Donald 5. Lilly July 8,1975

l 5 7 ABSTRACT A method for producing precipitated silicic acid pigmerits and silicates having a unique combination of physical and chemical properties is disclosed. The pigments are produced by acidulating a solution of an alkali metal silicate with an acid until precipitation just begins. At this point the reaction mass is aged for a period of time and thereafter the acid addition is continued until the precipitated product is obtained. Pigments produced in accordance with the invention exhibit lower wet cake moisture (or higher percent solids) and are characterized by their low structure, low oil absorption, high abrasiveness and high pack density. The products can be used as abrasive and polishing agents in dentifrice compositions, in the production of molecular sieves, in paints and the like. In a particularly advantageous embodiment, an adduct material, such as aluminum, is added to control the refractive index of the precipitated pigment. Products produced in this manner have particular utility for use as abrasion and gelling agents in clear toothpaste compositions.

1 Claim, 2 Drawing Figures a NON-1965B Phi/VENT I #7650 Low 6720677125 PIG-MENT 7, wETM/K MUISTl/EE 1 AMORPHOUS PRECIPITATED SILICEOUS PIGMENTS AND METHODS FOR THEIR PRODUCTION BACKGROUND OF THE INVENTION 1. Field of the invention The present invention relates to the production of precipitated silicas and. more particularly, to a novel process for producing synthetic precipitated silicas and silicates having new and improved physical and chemical properties.

2. Description of the Prior Art As known in the art. finely divided amorphous precipitated silicic acid pigments and cetain zeolitic type alumino silicates may be prepared by the acidulation of an aqueous silicate solution with an acid or a salt of the acid, such as aluminum sulfate. Such products are commercially available being sold e.g., under the trademarks Zeo"; Zeolex and Arogen" by the .l. M. Huber Corporation. Specific examples of these products as well as methods for their preparation are disclosed in US. Pat. Nos. 2,739,073; 2,843,346 and 3.582.379.

While the nature or characteristics of the above discussed precipitated silicic acid (sometimes herein referred to as silicas) and silicate pigments depend. in part. on the chemistry of the silicate solution (specifically the SiO /Na O ratio of the silicate) as well as the reaction conditions employed (precipitating pH. etc.). prior to the present invention such pigments were characterized by the following properties: high structure. high wet cake moisture content. high oil absorption. low valley abrasion, high surface area and low pack density. In this regard. and due in part to the properties such as high oil absorption, high surface area, etc.. the pigments have been widely and successfully used as reinforcing pigments in rubber. in paints. in the manufacture of paper. as moisture conditioners and the like.

However. and generally speaking for the moment. the high wet cake moisture content is disadvantageous in that the drying and filtration rates are increased thus increasing the overall cost in the production ofthe final product. For example. in the conventional production of silicic acid pigments as defined above the wet cake moisture content of the product (following filtration of the precipitated reaction mass) is approximately 82 percent. This means that there can be recovered only l8 parts of dry pigment from 100 parts of wet cake.

Further. and very importantly. the low abrasiveness and high refractive index of known silica and silicate pigments renders them unsuitable for many uses. For example. it is well known that conventional synthetic precipitated silicas are unsuitable as polishing and abrasive agents in tooth paste compositions. See German Pat. No. 974.958; French Pat. No. l,l30.627: British Pat. No. 995.351; Swiss Pat. No. 280.67l and US. Pat. No. 3.250.680. In this regard. it is disclosed in US. Pat. No. 3.538.230 that known amorphous silicas such as precipitated silicas. pyrogenic silicas and aerogels are unsuitable for dentifrice use because they show substantially no cleaning ability on human teeth because of their initial small particle size and because of the ease in which they break down into small particle sizes which result in poor cleaning ability.

Further. and in more detail, conventional silicas and amorphous precipitated alumino silicates, such as Zeolex and Arogen. cannot be used for a clear gel toothpaste because of their high refractive index 1.55) and because they lack the needed abrasive and polishing characteristics when added to the toothpaste base composition. Clear gel toothpaste contains a high percentage of abrasive and polishing agent in the toothpaste formula. The major function of the abrasive and polishing agent is to remove stains, food debris and bacterial plaque from the human tooth surface. Ideally the polishing agent should provide a maximum cleaning action at acceptable abrasion levels and must be compatible at high loadings of [5 up to 50 percent with other toothpaste formula ingredients. Thus known silicas and alumino silicates are unsuitable for clear gel toothpastes. (such as the product sold under the Trademark Close-Up" by Lever Brothers) because they cannot be added at high loadings of 15 percent and above in a typical toothpaste composition. Because of their high oil absorption, high sorption characteristics and high refractive index (L55) known precipitated pigments thicken up the dentifrice composition and impart undesirable opacity to the base paste resulting in an unac ceptable product. In summary of the above. precipi tated silicas and silicates cannot be used in conventional and clear gel dentifrice compositions because such products result in unacceptable toothpaste consistencies and do not possess the acceptable abrasive and polishing characteristics needed for use in dentifrice compositions.

SUMMARY OF THE lNVENTlON In summary. the present invention relates to the production of synthetic precipitated silicas and silicates having new and improved physical and chemical characteristics. More particularly. the invention is directed to a new and unique process for producing precipitated silicas and silicates having low structure. low wet cake moisture content. high abrasion. low surface area. low oil absorption and high pack densities. Because of such properties the improved pigments can be advantageously and effectively used as an abrasive and polishing agent in dentifrice compositions. In addition the new products can be advantageously employed in further applications such as in the preparation of molecular sieves. as flattening and texturizing agents. as fillers and carriers and as viscosity control agents.

Stated broadly. the method of the invention embodies the concept and is based on the discovery that if the addition of the acid to the silicate solution is inter rupted at the first appearance of the opalescence point (i.e.. that point at which precipitation first begins) the resulting pigments possess the aforementioned unique combination of properties. Stated differently. the low structure pigments of the invention are prepared by acidulating the aqueous alkali metal silicate solution (i.e.. sodium silicate) until precipitation just begins. At this point the reaction mass is aged for a suitable length of time generally on the order of from about l5 to 20 minutes. After the aging period, the introduction of the acid is continued until the precipitated product is obtained. In accordance with a further method embodiment it has been found that the properties of the pigment can be closely and accurately controlled if the acid and a portion of the alkali metal silicate are added simultaneously so that the reaction is carried out at an essentially constant pH. In accordance with a third and particularly advantageous method embodiment, the

cidulating agent. such as sulfuric acid. is pre-mixed with an adduct such as aluminum (which is preferably idded as a water soluble salt thereof, as e.g., aluminum ulfate). In this regard it has been found that the addiion of the adduct, coupled with the aging of the reacion mass. substantially controls the refractive index of he resulting pigment while at the same time not effectng the significant increase in the abrasiveness.

As briefly noted above, the precipitated pigments )roduced in accordance with the invention results in naterials of lower processing costs, better packaging :haracteristics and an unique balance of physical :hemical properties as compared to conventionally precipitated silicas.

It is accordingly a general object of the present invention to provide a novel process for producing precipitated silicas having improved physical and chemical properties.

Another and more particular object is to provide an unique process for producing synthetic amorphous precipitated siliceous pigments which have particular utility for use as abrasive and polishing agents in dentifrice compositions.

Yet another object is to provide a highly efficient and improved process for producing silicic acid pigment which exhibits lower wet cake moisture or higher percent solids and which have high valley abrasion and low oil absorption characteristics.

Yet still another object is to provide novel synthetic amorphous precipitated siliceous pigments which are useful as abrasion and gelling agents in clear toothpaste compositions.

A further object is to provide a new process for pro ducing precipitated amorphous silicas which have a unique balance of physical and chemical properties as compared to conventionally known precipitated pigments, said process further resulting in lower processing cost.

A still further object is to provide a process for producing low structure, low wet cake moisture, low surface area. low oil absorption, high valley abrasion and high pack density precipitated silicic acid pigments.

BRIEF DESCRIPTION OF THE DRAWINGS The manner in which the foregoing and other objects are achieved in accordance with the present invention will be better understood in view of the following detailed description and accompanying drawings, which form a part of the specification and wherein:

FIG. I is a graph showing the effect of the silicate mol ratio on the surface area of pigments produced in accordance with the invention and those produced by prior known techniques.

FIG. 2 is a graph showing the effect of the silicate mol ratio on the wet cake moisture content for pigments produced in accordance with the invention and those produced by prior techniques.

DESCRIPTION OF PREFERRED EMBODIMENTS As briefly discussed above, when an acid is added to a solution of an alkali metal silicate, the resulting reaction medium remains clear until such point that a slight turbidity (called the opalescence point) appears. As the acid addition is continued, the silicic acid or silica pigment starts precipitating until all of the silicate solution is precipitated. In conventionally known processes, the pH of the reaction mass is then adjusted to a range of from about 5.5 to 6.5 and the mass is filtered, washed and dried.

In accordance with the present invention. it has been discovered that if the acid addition is interrupted for a suitable period of time at the first appearance of opalescence, the resulting pigment possesses a unique combination of physical and chemical properties as well as improved processing advantages. More specifically and again as briefly noted above, the new silicic acid pigments produced in accordance with the invention exhibit lower wet cake moisture (or higher percent solids) thereby permitting increased drying and filtration rates. Further the new pigments have been found to have low structure, relatively low surface areas, low oil absorption, high pack densities and high valley abrasion. Because of these properties, the new pigments are particularly suitable and adapted for use as an abrasive and polishing agent in toothpaste compositions. Other properties include controlled particle size, better dispersion and improved wetting and viscosity characteristics.

At this point it may be noted that used herein the term structure" is intended to include, and is defined as, the ability of a silica or silicate material to hold water in its wet cake. When silicas or silicates such as the aforementioned conventional precipitated silicas, hold a high percentage of water i.e, in the neighborhood of to percent they are known and referred to as high structure silicas. Materials holding less than 70 percent and preferably in the neighborhood of from about 50 to 70 percent water in their wet cake are referred to as low structure silicas.

Turning now to more specific details, in the practice of the invention a solution of the alkali metal silicate is first charged to a reactor and the solution is heated to a temperature in the range of from about l00 to 200F, preferrably on the order of from about ISO to F. In general and except as otherwise expressly noted herein, the reaction temperatures and rates as well as the concentration of the reactants, i.e., the silicate solution and acid, are the same as in the above discussed known processes for producing precipitated si licic acid pigments. However, in the practice of the invention it has been found that particularly advantageous results are obtained if the concentration of the silicate solution is on the order of from about L0 to about 2.5 pounds/gallon. The acidulating agent or acid, e.g., sulfuric acid, is next charged to the reactor until the slight turbidity (ie. the opalescent point) first occurs. At this time the acid addition is stopped and the reaction is aged for a period of time on the order of from about 10 minutes to l hour. As to be discussed in more detail hereinafter, while the point or time at which the acidulation is discontinued is critical. it has been found that the aging period is generally dictated by process economics. For example, although the reaction mass must be aged for at least l0 minutes to obtain the aforementioned unique combination of properties, it has been found that aging for a period of longer than 2 hours does not, in fact, produce any particular advantage. Therefore from an economic standpoint, the aging period is preferably on the order of from about 10 to 15 minutes.

In accordance with one method embodiment of the invention, it has been found that a more homogeneous product can be obtained when from about one-half to two-thirds of the total silicate is initially charged to the reactor, and the remaining silicate is added simultaneously with the acid in a manner such that the reaction is carried out at a substantially constant ph. preferably on the order of from about 8.5 to I05. After the pigment has been precipitated, the pH of the resulting slurry is reduced to from about 5.5 to 7.0 by the addition of an excess of the acid.

In a further method embodiment. it has been found that the refractive index of the precipitated pigment can be controlled by the addition of an adduct element (such as aluminum, magnesium and the like) to provide an abrasive or polishing agent for a clear translucent or transparent toothpaste composition. Thus in this embodiment, the acid is premixed with a solution of the adduct material i.e., aluminum (preferably in the form of a water soluble salt such as aluminum sulfate, etc.) and the acidmetal salt mixture is then used for acidulating the aqueous alkali metal silicate until the precipitation just begins. At this point, and similarly as in the other embodiments. the acid and metal salt addition is interrupted and the reaction slurry is aged. After the aging, the addition of the acid-metal salt mixture is continued until the precipitation of the product is complete.

As will be seen from the above the starting materials or reactants employed in the present invention include alkali metal silicates, an acid and a water soluble metal salt. As used herein, the term alkali metal silicates include all the common forms of alkali silicates as, for example. metasilicates. disilicates and water glass. Water soluble potassium silicates and sodium silicates are particularly advantageous. Because of their relatively low cost, sodium silicates are preferred. lf employed, sodium silicates are effective in any composition in which the mole ratio of the SiO-, to Na,O is from about l to 4. In this regard commercially available sodium silicate solutions are more or less polymerized depending on their silica to sodium oxide (SiO /Na O) ratios. For example, sodium metasilicate solution (mole ratio unity) is known to be predominately monomeric in character while water glass (mole ratio 3.3) is both monomeric and polymeric in character. As the silica to sodium oxide mole ratio of sodium silicate increases. so does the polymer to monomer ratio of its silicate anions. While sodium silicates having a SiO /Na O mole ratio of from 1 to 4 may be employed. it has been found that particularly advantageous results are obtained in the SiO- ,/Na O ratio is in the range of from about 2.0 to 2.7.

While the acidulating agent or acid is preferably a strong mineral acid, such as sulfuric acid, nitric acid and hydrochloric acid, it should be understood that other acids, including organic acids, as for example, acetic acid. formic, or carbonic acid can be employed. The adduct material, employed to control the refractive index of the precipitated product may comprise metals such as aluminum, magnesium. zinc and calcium. However. the adduct is preferrably employed in the form of a water-soluble salt of the metal which should be compatible with the acid used for precipitation. For example. aluminum salts useful in the method of the invention are the water soluble salts of aluminum and strong acids such as aluminum sulfate, aluminum chloride. aluminum nitrate, and ammonium alum. The amount of the adduct or metal employed may vary depending upon the particular refractive index required. As shown in the following examples an excess of the adduct (e.g., AMSOU will increase the refractive index to a level above that required for clear dentifrice compositions (i.e., L475). However refractive indiees above L475 may be particularly suitable for many applications and the gist of this method embodiment lies in the discovery that the use of the adduct serves to control this property. The acidulating agent or acid is preferably added as a dilute solution thereof. Preferred results are obtained if the acidic solution is from about 10 to 25 percent by weight acid based on the total weight of the solution. However this may vary depending upon the particular acid employed, etc. The invention will be further illustrated by the following examples.

EXAMPLE I 30 gallons of a 1.24 No./gal. sodium silicate solution (SiO to Na O molar ratio of 2.5) was added to the stirred reactor and the silicate solution was heated to l. Sulfuric acid of 11.2 percent concentration was added to the reactor at the rate of 0.81 gallons per minute till a pH of I00 plus or minus 0.1 was reached. At this pH, the precipitation of silica micelles just started. The acid was shut off and the reaction medium was aged for l0 minutes. After the aging period, both acid and silicate were added simultaneously at the rate of 0.84 and L0 gallons per minute. The silicate was turned off after 30 minutes, the acid addition was continued and the batch was finished off at pH 5.8, filtered washed, dried and milled. The results of this and further examples are shown and summarized hereinbelow.

EXAMPLE 2 In this experiment. 35 gallons of 1.24 No./gal. silicate of SiO-; to Na O molar ratio of 2.5 were added to the stirred reactor and the silicate solution was heated to Sulfuric acid of l 1.4 percent concentration was added to the reactor at the rate of 0.84 gallons per minute till a pH of 10.1 plus or minus 0.l was reached. At this pH, the precipitation of silica micelles just started. The acid was shut off and the reaction medium was aged for IS minutes. The aging step is important to ob tain homogeneous product and for the silica micelles to reach an equilibrium condition. After the aging period, both acid and silicate were added simultaneously at the rate of 0.84 and L4 gallons per minute. Silicate was turned off after 25 minutes; acid addition was continued and the batch was finished off at pH 5.5. filtered. washed dried and milled. in further tests it was found that a range of products can be made be introducing more than one aging step during the process and by maintaining the precipitation pH substantially constant and within the range of pH 7-l0.

EXAMPLE 3 in this experiment. 10 gallons of l.24 No./gal. sodium silicate of SiO to Na O molar ratio of 2.5 were added to a stirred reactor and the solution heated to 175. Sulfuric acid of l l.4 percent concentration was added to the reactor at the rate of 0. l2 gallons per minute until the silica just started precipitating. At that time the reaction pH was l0.l. The acid addition was stopped and the reaction medium was aged for 15 minutes. After the aging period. the acid addition was resumed again until the reaction pH of 9.0 was achieved. At this point the acid was stopped again for IS minutes and the reaction medium was aged. After aging period was over. silicate was only added to the reactor at the rate of 0.1

gallons per minute until pH of 10.1 was reached. Acid addition was resumed again and the batch was finished off at pH 5.7. The idea of aging at pH 9.0 was to have the silica particles grow to a bigger size and to obtain a final product with lower structure. lower surface area and higher pack density than the conventional silica.

EXAMPLE 4 In this example. five gallons of 1.24 Nojgal. sodium silicate of SiO to Na O molar ratio of 2.5 were added to the stirred reactor and the silicate was heated to 175. Acid of 10.5 percent concentration was added to the silicate till a turbidity or faint precipitation appeared in the reactor. Acid was stopped at this point and the reaction medium was aged for 20 minutes. After the aging period, 5 gallons of silicate and 11.4 percent acid were added simultaneously at the rate of 0.20 to 0.12 gallons per minute and the batch was finished off at pH 5.5. filtered, washed. dried and milled.

EXAMPLE 5 The procedure of Example 4 was repeated except that 6 gallons of silicate were added to the reactor and the remaining 4 gallons were added after the aging period along with the acid.

EXAMPLE 6 The procedure of Example 4 was repeated except that seven gallons of silicate were added to the reactor and the remaining 3 gallons were added simultaneously with acid after aging the reaction medium. The batch was processed similar to Example 4.

EXAMPLE 7 The procedure of Example 2 was repeated except that after the aging period, the precipitation pH was controlled at pH 9.9 plus or minus 0.1. The batch was finished and processed similar to Example 2.

EXAMPLE 8 The procedure of Example 4 was repeated except that the finishing pH was brought down to 3.2. Lower finishing pH results in product of higher surface area.

EXAMPLE 9 and the batch was processed similar to Example 4 above.

EXAMPLE 10 A control batch of conventional precipitated silica was prepared by neutralizing 1.24 Nojgal. sodium silicate with 1 1.4 percent acid till the final pH of 5.5 was obtained. In the control batch no aging step was involved so that the properties of material produced via the new process could be compared with the control batch.

Data on precipitated silicas obtained in Examples 1 thru 10 are summarized below:

/1 Sun Oil Density Valley Ex- Dcs- Wct l'acc Absorp Pour. Abraamcrip- Cake Area tion Pack sion plc tion Moisture (m /g1 cc/100g [lb/cult) mg loss 1 Silica 66 85 11.2 18.7 15.0

via aging 2 Silica 55 38 81 14.2 27.7 17.]

via aging 3 Silica 70 66 9.9 19.5 6.7

via aging 4 Silica 53 29 66 18.4 33.7 83.5

via aging 5 Silica 59 116 108 14. 26.0 15.3

via aging 6 Silica 59 46 108 13.9 26.0 16.3

via aging 7 Silica 62 S3 125 222 18.8

via aging ii Silica 60 242 12.7 3.9 28.4

via aging 9 Silica 56 38 81 17.8 29.7 18.6

via aging 10 Control 82 150 211 6.3 10.7 2.5

(an aging) From the above data, it is clear that the new process of the invention results in silicas of lower wet cake moisture. lower structure. lower oil absorption, lower surface area. higher pack density and higher valley abrasion than conventional precipitated silicas.

The new process leads to silicas of lower processing costs than regular precipitated silicas. For example, the average wet cake moisture of silicas via the new process is only 60 percent as opposed to 82 percent for regular silica (see control). This means we can recover 40 parts of dry silica from parts of wet cake if the silica is produced via the new process. Regular processes result in recovery of about 1 8 parts of dry silica per 100 parts of wet cake. Thus. via the new process we can recover 22 parts or more of dry silica or an increase of (22/I8) X 100 or 122 percent. The new process results in silicas of better drying and filtration rates and hence significantly lower processing costs than the precipitated silicas produced by the conventional process.

EXAMPLE 1 1 in a series of tests the general procedures of Exampies 1-10 were repeated except that the precipitating pH and the period of aging were varied. The pH was varied in the range of from about 5.5 to l 1.0. The aging period was varied from about 5 minutes to 1 hour. The results of these tests were substantially the same as that of Examples l-lt) except that it was found that prodacts of predetermined properties and characteristics (i.e.. a specific structure or wet cake moisture content) could be obtained by varing the above process conditions within the specified ranges. These tests also established that if the final batch pH was reduced to below about 5.0 an increase in the surface area was obtained. Thus if it is desired that the final product have a low surface area then the pH of the final batch should be maintained above 5.0. Also these tests established that aging for periods of less than about 8-10 minutes was generally ineffective to produce the low structures, etc. products of the invention.

range of about 7-l0.

EXAMPLE EXAMPLE 12 A control experiment was performed by using the The general procedure of Examples ll l were re- 5 precipitation procedure of Example 14, but by using no peated except that nitric acid, hydrochloric acid. acetic aging 5[ep acid and formic acid were substituted for the sulfuric acid. The results were substantially the same as in Ex- EXAMPLE ampleS F1 The procedure of Example 14 was repeated except EXAMPLE l3 the acid aluminum sulfate ratio was vari ed by mixing 100 parts of l 1.4 percent sulfuric acid with l 1.4 parts In a series of tests the general procedures of Examf 138 pounds per ll l i lf ples l12 were repeated except that aqueous sodium silicates having mol ratios (SiO /Na O) in the range of EXAMPLE I7 from I to 4 were substituted for the 2.5 silicate of EX- 15 A control experiment was performed as per the proamples 1-12. The results were substantially the same as cedure of Example 16, but without using the aging step. above except that it was found that the wet cake moisture content was lower when the 2.5 silicate was em- EXAMPLE ployed. In addition the surface area was found to be E l 14 was ated by ing a id-al min m Substantially lower when m0] Silicate was sulfate mixture of 100 parts of acid to five parts of aluployedv In this regard, in a series of tests the wet cake minum sulfate. moisture content and the surface area were com ared for silicic acid pigments produced by prior known iech- EXAMPLE niques (non-aged) and products produced in accor- A control experiment was performed as per the prodance with the present invention. The results are shown cedure of Example 18 but without using the aging step. in FIGS. 1 and 2.

The following Examples serve to illustrate the third EXAMPLE 20 method embodiment of the invention, i.e., the addition The procedure of Example 14 was repeated except of the adduct material to control the refractive index. that the acid and aluminum sulfate were pre-mixed in EXAMPLE 14 the ratio of 100.7.0.

In this experiment 100 parts by volume of 11.4 per- LE 21 Cent Sulfuric a was pre'miifed w 3 Parts of The procedure of Example 14 was repeated but only Nolgal. aluminum sulfate. This acid-aluminum sulfate 2 acid was added up to h i g step. After the aging pem'xwre was used F P the fflumma S'hcate of riod. acid, silicate, and aluminum sulfate were added ?f Index Thrty'five gzfnens of simultaneously to the reactor. Both the silicate and aluheme 9 SIO'J m N320 molar W Of2'6 minum sulfate additions were discontinued after 25 "(med m the smroed reflctor P [he 301mm" minutes. Acid addition was continued until final pH of heme! m 175 M'Xed acdulummum sulfate 40 5.5 was obtained. The batch was processed similar to lution was added to the reactor at the rate of 0.84 gal- ExamP'e l3. lons per minute until reaction pH of 10.1 plus or minus 0.1 was reached. At this pH, the precipitation of alumi Example 2 num silicate micelles just started. The acid-aluminum sulfate addition was discontinued and the reaction me- The pljocedwe of EmmPle was repeats? except dium was aged for 15 minutes. The aging or digestion that sodium silicate contained 3 percent sodium sul- Step was found to be important to obtain a homogene fate. The effect of sodium sulfate was that the final ous product and for the alumino silicate micelles to product mme abraswe than one produced m reach an equilibrium condition. After the aging period, example both acid-aluminum and silicate solutions were added simultaneously at the rate of 0.84 and 1.4 gallons per EXAMPLE 23 minute, respectively. Silicate addition was turned off The procedure of Example 14 was repeated except after 25 minutes; mixed acid-aluminum sulfate addition that acid-aluminum sulfate were pre-mixed in the ratio was continued and the batch was finished off at pH 5.5, 100 to 2.5. filtered. washed. dried and milled in the conventional The following Table summarizes the data obtained in manner. In a series of tests it was found that a range of Examples 14-23. From the following it will be seen that products could be made by introducing more than one silicate pigments of controlled refractive index and aging step during the process and by maintaining the abrasiveness can be tailored by way of the process of precipitation pH substantially constant and within the this invention.

TABLE I (m /g) Oil Val- R Sur- Abs. Iey Refract Exface (cc. Abraive ample Description A1203 WCM Area 100g) sion Index 14 SAS via aging 0.69 I06 15.0 1.450 15 Control-no aging 0.69 79 161 203 2.7 1.446 16 SAS via aging 2.12 58 295 99 15.9 1.464 17 Control-no aging 2.12 76 250 203 3.6 1.464

TABLE 1 Cntinued (m /g) Oil Val- R Sur- Abs. ley Refract- Exface (cc. Abraive ample Description Al,O WCM Area 100g) sion Index 18 SAS via aging 0.90 56 198 B l7.l 1.451 19 Control-no aging 0.90 79 232 2l9 2.3 l.45l 20 SAS via aging L20 58 246 90 5.3 L454 21 SAS via aging (1.70 58 202 99 9.0 1.448 22 SAS via aging 0.73 55 I ll 80 59.5 1.437 23 SAS via aging 56 87 74 11.5 1.450

SAS is Sodium Alumino Silicate.

From the above date. it will be seen that the new pro cess results in alumino silicates of lower structure, lower wet cake moisture. lower oil absorption and higher valley abrasion than the conventional precipitated alumino silicates. Note that the controls of Examples l5. l7 and l9 exhibit high oil absorption and low valley abrasions and hence cannot be used for clear gel toothpaste because they provide unacceptable abrasion characteristics and thicken up the toothpaste base even at low loadings of up to only 8 percent. In general refractive indiees of from about L445 to L475 are needed and required for clear gel cosmetic dentifrice use.

EXAMPLE 24 in a series of tests the general procedures of Examples l4-23 were repeated except that nitric acid, hydrochloric acid. acetic acid and formic acid were substituted for the sulfuric acid. The results were substantially the same as in Examples l424.

EXAMPLE 25 in a series of further tests the procedures of Examples 14-24 were repeated except that the precipitating pH. the period of aging as well as the SiO INa O mol ratio of the silicate were varied in the manner as shown in Examples lll3. The results were substantially the same except with regard to those variables and results noted in Examples ll-l3 and FIGS. 1 and 2.

EXAMPLE 26 The general procedures of Examples l-25 were repeated except that potassium silicate was substituted for the sodium silicate. The results were substantially the same as in Examples 1-25.

EXAMPLE 27 In this experiment the determination and variables associated with the first occurance of the opalescence point as well as the importance of the aging" at this point. were investigated. The study revealed that a crit ical step in producing an acceptable aged pigment is the determination of the opalescence point. For a given batch. the appearance of the opalescence point depends on the following:

Silicate concentration Silicate mol ratio Sulfuric acid concentration Sulfuric acid rate The development work on aged pigment was done by adding 11.4 percent sulfuric acid at the rate of 450 cc/min to 10 gallons of 2.5 mol ratio silicate of l3.3 percent concentration. The opalescence point appeared at 21 minutes and 15 seconds of acid addition. When the same batch was prepared with silicate of mol ratio 2.68, the opalescence point appeared at 19 minutes and 30 seconds. The processing advantages of the invention were found to be directly related to the determination of the opalescence point. lf the reaction me' dium is aged by stopping acid about 30 seconds after the appearance of opalescence point. then about percent of the process advantages are lost. By aging the reaction medium 60 seconds after the opalescence point. lOO percent of the processing advantages are lost and the product has properties similar to those produced by prior known processes. lf the reaction medium is aged after stopping acid about 30 seconds be fore the opalescence point then an unacceptable product that is slow filtering and which exhibits significant changes in properties is obtained. Thus, an acceptable product can be produced only by stopping the acid addition and aging the reaction medium as soon as the opalescence point appears.

In this regard a Bailey, high range bolometer, was hooked up to the pigment reactor to detect the opales cence point. [t was observed that such a sensing device can be used effectively in detecting the opalescence point. It is important that the bolometer chamber be free of air bubbles; otherwise. a false opalescence point will be registered.

The following table (2] is a summary of the results of this study.

TABLE 2 Oil 7% Absorption MR. Final WCM Emm /g) (cc oil/100g) Silicate pH Remarks* 38 t ll 268 5.9 l 58 l 10 76 2.68 5.5 2 59 95 85 2.68 5.5 1 63 75 9U 2.68 5.4 4

I=Aging done by stopping acid .it upalescencc 2=Aging dune by stopping acid at seconds before opaicsccnce point 3=Aging done h stopping ncld 3U seconds after opalesccncc point =Aging done by stopping acid till seconds after opnlcscencc point From the above it will be seen that the process of the instant invention results in a new product having a unique combination of physical and chemical proper ties. These include. e.g., low absorption, i.e., on the order of less than l25 cc/l00 gm. wet cake moisture contents of less than percent, surface areas of less than lOO m lg when the adduct material is not added and in the range of from about l00-3OO when the latter is employed; pack densities of greater than l2 No./ft and valley abrasions of greater than 5 (mg. wire loss). Improved and very important processing advantages are also obtained. While particular embodiments have been disclosed for illustrative purposes the invention is not intended to be limited thereto. For example, in the case of pigment production for a special utility the precipitating pH and the final slurry pH may be tailored accordingly. Also, and as should be readily appreciated by those skilled in the art. no special equipment is required in the method herein described. In this regard.

however. the reactor should be equipped with heating means. eg. a steam jacket. in order to maintain the desired reaction temperature and should have adequate agitating means to produce a strong backflow on the body of the liquid and thus avoid zones of high concentration of the incoming reactants. lt is desirable to bring the reactants together so to produce an instantaneous reaction of all material being fed to the fullest extent reasonably possible, as such promotes uniformity of the resulting products. Storage vessels (for the reactants) connected to the reaction vessel thru lines fitted with flow control means may also be provided. The reaction vessel may be equipped with an outlet line leading to a filter which may be of conventional design. As noted above. the filtered mass is washed and dried. Such steps may also be conducted in conventional equipment it being understood. of course, that same do not form a part of the present invention.

ll" the pigments of the invention are used in tooth paste compositions. the dentifrice (if in the form of a paste) may contain humectant materials and binders to give the dentifrice a smooth texture and good flowahility. Glycerine, sorbitol. corn syrup glucose and the like may be used as carriers. Examples of binders include gum tragacanth, sodium carboxy-methylcellulose and the like. The above materials as well as the specific formulation of the toothpaste are well known in the art and are disclosed for example in U.S. Pat. Nos. 2.994.642 and 3,538,230 and numerous publications.

What is claimed is:

l. A new composition of matter comprising an amorphous, finely divided precipitated silica pigment having a wet cake moisture content of less than 70 percent; a surface area of less than 100 m lg; an oil absorption on the order of less than l25cc/l00 gm; pack densities of greater than l2 pounds/cu. ft. and a valley abrasion of greater than 5.0 mg. wire loss.

UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION 3,893 ,840 July 8 1975 Patent No. Dated Satish K. Wason lnventor(s) It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:

Column 1, line 15, "cetain" should read certain Column 5, 1ine117, "acidmetal" should read acid-metal w.

Column 6, line 19, following "185" insert F fourth line of Ex. 2: following "175" insert v F 1 line 48, following "washed" insert w 1:;

line 57, following "175" insert F Column 7, line 11, following "175" insert F 5 first line of Ex. 9, "1.24 No./gal. should read 1.24 1bs./gal.

third line of EX. 9, following "175" insert F second line of Ex, 10, "1/24 No./ga1." should read 1:

1.24 lbs./gal.

Signed and Scaled this sixth D y of January 1976 [SEAL] Arrest:

RUTH C. MASON C. MARSHALL DANN Arlesn'ng Officer Commissioner of Parents and Trademarks UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION PATENT NO. 3,893,840 DATED July 8, 1975 TNVENTORtS) Satrsh K. wason Col Col

Col

Col

Col

Col

It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below;

Isa/u.)

line 3: "ph" should read pH line 16: "1.24 No./gal." should read l.24 lbs./gal.

first line of Ex. 2: "l.24 No./gal." should read l.24 lbs./gal. line 49: "be" (second instance) should read by line 55: "l.24 No./gal." should read l.24 lbs./gal.

line 9: "l.24 N0./gal." should read l.24 lbs./gal.

lT'ne 60: "varr'ng" should read varying Signed and Sealed this Thirteenth Day of July 1976 A rte: t:

RUTH C. MASON Arresting Officer C. MARSHALL DANN (nmmim'uner nj'larenm and Trademark: 

1. A NEW COMPOSITION OF MATTER COMPRISING AN AMORPHOUS, FINELY DIVIDED PRECIPTATED SILICA PIGMENT HAVING A WET CAKE MOISTURE CONTENT OF LESS THAN 70 PERCENT, A SURFACE AREA OF LESS THAN 100 M2/G: AN OIL ABSORPTION ON THE ORDER OF LESS THAN 